Solid LD-B coupling agent is developed by our company with help of a famous chemical expert’s guidance. It has been playing an 

important role in the field of solid material since put on the market. The application scope of this product is wide. It has excellent 

surface active-treating ability. It possesses advantages like high whiteness、odorlessness and nice dispersion.

First, product information

Appearance: White or milk white powder solid

Melting Temperature: Less than 70℃

Thermal Decomposition Temperature: More than 250℃

Mechanical Impurities: Less than 0.02%

Virulence: Non-toxic

Second, application scope

The product is suitable for various kinds of powder materials or fillers, such as: light/heavy calcium carbonate, argil, mica powder, 

wollastonite, talcum powder or pigment’s surfactant, also suitable for plastic, rubber, coating, inks and binder which can add 

coupling agent directly.

Third, features

Compared with similar products, it has better synergy stability and lubricity. The application scope is wide with small addition 

volume, convenient usage and low price.

Fourth, usage and consumption

A、 Pretreatment Method: 

 Put the powder/filler into high-speed kneader preheating to 110℃, drying the moisture in the powder/filler. 

Then add the calculated coupling agent and the treatment time is about 8-10 minutes 

(If needed, other agents should be added after the coupling agent, about 4 minutes later). 

It is forbidden to use the product together with other dispersing agent.

B、 Direct addition:

The coupling agent can be added directly when mixing at a high speed, the method is the same as above. 

But attention should be paid to the components which contain carboxyl, hydroxy like stearic acid and organic alcohol 

as they should be added 3-4 minutes later after coupling agent’s activation modification to powder. 

In the above methods, the former has the better effect.

Consumption:

1. For normal filler, 0.8-1.0% of filler

2. For thin film master batch, 1.5-2.0% of filler

3. For powder material, 1.0-1.5% of powder

4. For color matrix, cable material，1.5-3.0% of filler

5. For PVC products, 1.0-1.5% of filler

6. For hard PVC products, 0.5-1.0%

7. For coatings and inks, 0.7-1.5%

Fifth, attention

1. For composite product which use granulous resin as material, like PE, PP, ABC and PC, firstly make this product in 

master batch or granules form, then mix with these resin;

2. Keep it away from water and fire and keep it dry. If sealed off, use it as soon as possible, or sealed again. 

3. Used up within the best valid period (half year is recommended).

Sixth, packing

500g/bag （polythene film bag）, 40bags/ box, total net weight is 20kg.  